压力单位换算和腐蚀材质表
更新时间：2008-09-23 点击次数：3199
| 压力单位换算表 | | 单位 | Pa | KPa | MPa | bar | mbar | kgf/cm2 | cmH2O | mmH2O | mmHg | p.s.i | | Pa | 1 | 10-3 | 10-6 | 10-5 | 10-2 | 10.2×
10-6 | 1.02×10-3 | 101.97×
10-3 | 7.5×
10-3 | 0.15×10-3 | | KPa | 103 | 1 | 10-3 | 10-2 | 10 | 10.2×
10-3 | 10.2 | 101.97 | 7.5 | 0.15 | | MPa | 06 | 103 | 1 | 10 | 104 | 10.2 | 1.02×103 | 101.97×103 | 7.5×103 | 0.15×103 | | bar | 105 | 102 | 10-1 | 1 | 103 | 1.02 | 1.02×103 | 10.2×103 | 750.06 | 14.5 | | mbar | 102 | 10-1 | 10-4 | 10 | 1 | 1.02×
10-3 | 1.02 | 10.2 | 0.75 | 14.5×10-3 | | kgf/cm2 | 98066.5 | 98.07 | 98.07×
10-3 | 0.98 | 980.67 | 1 | 1000 | 10.000 | 735.56 | 14.22 | | cmH2O | 98.06 | 98.07×
10-3 | 98.07×
10-6 | 0.98×
10-3 | 0.98 | 10-3 | 1 | 10 | 0.74 | 14.22×103 | | mmH2O | 9.806 | 9.807×
10-3 | 9.807×
10-6 | 98.07×
10-6 | 98.07×
10-3 | 10-4 | 0.1 | 1 | 73.56×
10-3 | 1.42×10-3 | | mmHg | 133.32 | 133.32×
10-3 | 133.32×
10-6 | 1.33×
10-3 | 1.33 | 1.36×
10-3 | 1.36 | 13.6 | 1 | 19.34×10-3 | | p.s.i | 6894.76 | 6.89 | 6.89×
10-3 | 68.95×
10-3 | 68.95 | 70.31×
10-3 | 70.31 | 703.07 | 51.71 | 1 | | | | |
| 关于隔离膜片部分耐蚀材料的选择 | | 腐蚀介质 | 耐腐蚀材料 | | 锡青铜(QSn6.5-0.4) | SUS316 | 纯钽(Ta) | 蒙耐尔(Ni70Cu30) | 哈氏合(HC) | 聚四氟乙烯（F4） | | 硫酸（H2SO4） | V | △ | ○ | V | V | V | | 硝酸（HNO3） | ╳ | V | ○ | ╳ | V | V | | 盐酸（HCI） | △ | ╳ | ○ | ╳ | V | V | | 磷酸（H3PO4） | V | V | ○ | V | V | V | | 醋酸（CH3COOH） | V | V | ○ | V | ○ | V | | 烧碱（NaOH） | △ | ○ | △ | ○ | ○ | V | | 纯碱（Na2CO3） | ○ | ○ | ○ | ○ | V | V | | 小苏打（NaHCO3） | V | ○ | ○ | ○ | ○ | V | | 氯气（CI） | 干：V
湿：╳ | 干：V
湿：╳ | ○ | 干：V
湿：╳ | V | V | | 溴（Br2） | 干：△
湿：╳ | 干：╳
湿：△ | ○ | 干：○
湿：╳ | ○ | V | | 氨水（NH3） | ╳ | V | ╳ | ╳ | ○ | V | | 海水（30％ NaCI） | V | V | ○ | ○ | ○ | V | | 符号说明：○——*；△——有条件使用；V——可以使用；╳——不可以使用。 |
本公司一般的选用材料为SUS316-0Cr17Ni12m，以上耐蚀材料选择为常温情况，对在特殊情况下耐蚀材料的选择请与我公司具体垂询。
| |